Grade CW12MW Nickel vs. C14300 Copper
Grade CW12MW nickel belongs to the nickel alloys classification, while C14300 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade CW12MW nickel and the bottom bar is C14300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 4.6 | |
| 2.0 to 42 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 85 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 220 to 460 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 76 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 960 | |
| 220 |
| Melting Completion (Liquidus), °C | 1610 | |
| 1080 |
| Melting Onset (Solidus), °C | 1560 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 390 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 31 |
| Density, g/cm3 | 9.1 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 2.6 |
| Embodied Energy, MJ/kg | 180 | |
| 41 |
| Embodied Water, L/kg | 280 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 22 | |
| 9.0 to 72 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 25 to 810 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 18 |
| Strength to Weight: Axial, points | 17 | |
| 6.8 to 14 |
| Strength to Weight: Bending, points | 17 | |
| 9.1 to 15 |
| Thermal Shock Resistance, points | 16 | |
| 7.8 to 16 |
Alloy Composition
| Cadmium (Cd), % | 0 | |
| 0.050 to 0.15 |
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.9 to 99.95 |
| Iron (Fe), % | 4.5 to 7.5 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 16 to 18 | |
| 0 |
| Nickel (Ni), % | 49.2 to 60.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 3.8 to 5.3 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.4 | |
| 0 |