Grade CW12MW Nickel vs. C92300 Bronze

Grade CW12MW nickel belongs to the nickel alloys classification, while C92300 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade CW12MW nickel and the bottom bar is C92300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 4.6
19
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 85
40
Tensile Strength: Ultimate (UTS), MPa 560
300
Tensile Strength: Yield (Proof), MPa 310
140

Thermal Properties

Latent Heat of Fusion, J/g 320
190
Maximum Temperature: Mechanical, °C 960
170
Melting Completion (Liquidus), °C 1610
1000
Melting Onset (Solidus), °C 1560
850
Specific Heat Capacity, J/kg-K 410
370
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 70
33
Density, g/cm3 9.1
8.7
Embodied Carbon, kg CO2/kg material 13
3.4
Embodied Energy, MJ/kg 180
56
Embodied Water, L/kg 280
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
47
Resilience: Unit (Modulus of Resilience), kJ/m3 220
86
Stiffness to Weight: Axial, points 13
6.9
Stiffness to Weight: Bending, points 22
18
Strength to Weight: Axial, points 17
9.5
Strength to Weight: Bending, points 17
11
Thermal Shock Resistance, points 16
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 15.5 to 17.5
0
Copper (Cu), % 0
85 to 89
Iron (Fe), % 4.5 to 7.5
0 to 0.25
Lead (Pb), % 0
0.3 to 1.0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 16 to 18
0
Nickel (Ni), % 49.2 to 60.1
0 to 1.0
Phosphorus (P), % 0 to 0.040
0 to 1.5
Silicon (Si), % 0 to 1.0
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.050
Tin (Sn), % 0
7.5 to 9.0
Tungsten (W), % 3.8 to 5.3
0
Vanadium (V), % 0.2 to 0.4
0
Zinc (Zn), % 0
2.5 to 5.0
Residuals, % 0
0 to 0.7