Grade CW12MW Nickel vs. C95600 Bronze

Grade CW12MW nickel belongs to the nickel alloys classification, while C95600 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade CW12MW nickel and the bottom bar is C95600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 4.6
15
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 85
42
Tensile Strength: Ultimate (UTS), MPa 560
500
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Maximum Temperature: Mechanical, °C 960
210
Melting Completion (Liquidus), °C 1610
1000
Melting Onset (Solidus), °C 1560
980
Specific Heat Capacity, J/kg-K 410
430
Thermal Expansion, µm/m-K 12
17

Otherwise Unclassified Properties

Base Metal Price, % relative 70
28
Density, g/cm3 9.1
8.3
Embodied Carbon, kg CO2/kg material 13
3.0
Embodied Energy, MJ/kg 180
50
Embodied Water, L/kg 280
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
60
Resilience: Unit (Modulus of Resilience), kJ/m3 220
230
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 22
19
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 17
17
Thermal Shock Resistance, points 16
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
6.0 to 8.0
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 15.5 to 17.5
0
Copper (Cu), % 0
88 to 92.2
Iron (Fe), % 4.5 to 7.5
0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 16 to 18
0
Nickel (Ni), % 49.2 to 60.1
0 to 0.25
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
1.8 to 3.2
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 3.8 to 5.3
0
Vanadium (V), % 0.2 to 0.4
0
Residuals, % 0
0 to 1.0