Grade CW6MC Nickel vs. AWS BAu-3

Grade CW6MC nickel belongs to the nickel alloys classification, while AWS BAu-3 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is grade CW6MC nickel and the bottom bar is AWS BAu-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.29
0.37
Shear Modulus, GPa 79
41
Tensile Strength: Ultimate (UTS), MPa 540
220

Thermal Properties

Latent Heat of Fusion, J/g 330
160
Melting Completion (Liquidus), °C 1480
1030
Melting Onset (Solidus), °C 1430
970
Specific Heat Capacity, J/kg-K 440
300
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Density, g/cm3 8.6
13

Common Calculations

Stiffness to Weight: Axial, points 13
5.0
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 18
4.9
Strength to Weight: Bending, points 17
6.4
Thermal Shock Resistance, points 15
8.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 20 to 23
0
Copper (Cu), % 0
60.9 to 63
Gold (Au), % 0
34.5 to 35.5
Iron (Fe), % 0 to 5.0
0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 55.4 to 68.9
2.5 to 3.5
Niobium (Nb), % 3.2 to 4.5
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Residuals, % 0
0 to 0.15