Grade CW6MC Nickel vs. EN 1.1158 Steel

Grade CW6MC nickel belongs to the nickel alloys classification, while EN 1.1158 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade CW6MC nickel and the bottom bar is EN 1.1158 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
23 to 24
Fatigue Strength, MPa 210
170 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 540
470 to 500
Tensile Strength: Yield (Proof), MPa 310
240 to 310

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 11
49
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 80
2.1
Density, g/cm3 8.6
7.8
Embodied Carbon, kg CO2/kg material 14
1.4
Embodied Energy, MJ/kg 200
19
Embodied Water, L/kg 290
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
89 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 240
150 to 250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
17 to 18
Strength to Weight: Bending, points 17
17 to 18
Thermal Diffusivity, mm2/s 2.8
13
Thermal Shock Resistance, points 15
15 to 16

Alloy Composition

Carbon (C), % 0 to 0.060
0.22 to 0.29
Chromium (Cr), % 20 to 23
0 to 0.4
Iron (Fe), % 0 to 5.0
97.6 to 99.38
Manganese (Mn), % 0 to 1.0
0.4 to 0.7
Molybdenum (Mo), % 8.0 to 10
0 to 0.1
Nickel (Ni), % 55.4 to 68.9
0 to 0.4
Niobium (Nb), % 3.2 to 4.5
0
Phosphorus (P), % 0 to 0.015
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035