Grade CX2M Nickel vs. AWS ERNiCrFe-5

Both grade CX2M nickel and AWS ERNiCrFe-5 are nickel alloys. They have 77% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is grade CX2M nickel and the bottom bar is AWS ERNiCrFe-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 45
34
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 84
74
Tensile Strength: Ultimate (UTS), MPa 550
630

Thermal Properties

Latent Heat of Fusion, J/g 330
310
Melting Completion (Liquidus), °C 1500
1390
Melting Onset (Solidus), °C 1450
1340
Specific Heat Capacity, J/kg-K 430
450
Thermal Conductivity, W/m-K 10
14
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 65
65
Density, g/cm3 8.7
8.5
Embodied Carbon, kg CO2/kg material 12
11
Embodied Energy, MJ/kg 160
150
Embodied Water, L/kg 310
250

Common Calculations

Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 2.7
3.6
Thermal Shock Resistance, points 15
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.020
0 to 0.080
Chromium (Cr), % 22 to 24
14 to 17
Cobalt (Co), % 0
0 to 0.12
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 0 to 1.5
6.0 to 10
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 15 to 16.5
0
Nickel (Ni), % 56.4 to 63
70 to 78.5
Niobium (Nb), % 0
1.5 to 3.0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.35
Sulfur (S), % 0 to 0.020
0 to 0.015
Residuals, % 0
0 to 0.5