Grade CX2M Nickel vs. EN 1.7108 Steel
Grade CX2M nickel belongs to the nickel alloys classification, while EN 1.7108 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade CX2M nickel and the bottom bar is EN 1.7108 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 670 to 2070 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 410 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1430 |
| Melting Onset (Solidus), °C | 1450 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 480 |
| Thermal Conductivity, W/m-K | 10 | |
| 46 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 2.1 |
| Density, g/cm3 | 8.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 1.5 |
| Embodied Energy, MJ/kg | 160 | |
| 20 |
| Embodied Water, L/kg | 310 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 18 | |
| 24 to 75 |
| Strength to Weight: Bending, points | 17 | |
| 22 to 47 |
| Thermal Diffusivity, mm2/s | 2.7 | |
| 12 |
| Thermal Shock Resistance, points | 15 | |
| 20 to 63 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0.57 to 0.65 |
| Chromium (Cr), % | 22 to 24 | |
| 0.2 to 0.45 |
| Iron (Fe), % | 0 to 1.5 | |
| 95.9 to 96.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 15 to 16.5 | |
| 0 |
| Nickel (Ni), % | 56.4 to 63 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 1.6 to 2.0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.025 |