Grade CX2M Nickel vs. N06035 Nickel

Both grade CX2M nickel and N06035 nickel are nickel alloys. They have 88% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade CX2M nickel and the bottom bar is N06035 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
210
Elongation at Break, % 45
34
Fatigue Strength, MPa 260
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 84
84
Tensile Strength: Ultimate (UTS), MPa 550
660
Tensile Strength: Yield (Proof), MPa 310
270

Thermal Properties

Latent Heat of Fusion, J/g 330
340
Maximum Temperature: Mechanical, °C 990
1030
Melting Completion (Liquidus), °C 1500
1440
Melting Onset (Solidus), °C 1450
1390
Specific Heat Capacity, J/kg-K 430
450
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 65
60
Density, g/cm3 8.7
8.4
Embodied Carbon, kg CO2/kg material 12
10
Embodied Energy, MJ/kg 160
140
Embodied Water, L/kg 310
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
180
Resilience: Unit (Modulus of Resilience), kJ/m3 220
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 17
20
Thermal Shock Resistance, points 15
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0 to 0.020
0 to 0.050
Chromium (Cr), % 22 to 24
32.3 to 34.3
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 1.5
0 to 2.0
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 15 to 16.5
7.6 to 9.0
Nickel (Ni), % 56.4 to 63
51.1 to 60.2
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.020
0 to 0.015
Tungsten (W), % 0
0 to 0.6
Vanadium (V), % 0
0 to 0.2