Grade CX2M Nickel vs. N10624 Nickel

Both grade CX2M nickel and N10624 nickel are nickel alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade CX2M nickel and the bottom bar is N10624 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
220
Elongation at Break, % 45
45
Fatigue Strength, MPa 260
310
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 84
84
Tensile Strength: Ultimate (UTS), MPa 550
810
Tensile Strength: Yield (Proof), MPa 310
360

Thermal Properties

Latent Heat of Fusion, J/g 330
320
Maximum Temperature: Mechanical, °C 990
930
Melting Completion (Liquidus), °C 1500
1580
Melting Onset (Solidus), °C 1450
1520
Specific Heat Capacity, J/kg-K 430
410
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 65
70
Density, g/cm3 8.7
9.0
Embodied Carbon, kg CO2/kg material 12
13
Embodied Energy, MJ/kg 160
170
Embodied Water, L/kg 310
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
300
Resilience: Unit (Modulus of Resilience), kJ/m3 220
300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 18
25
Strength to Weight: Bending, points 17
22
Thermal Shock Resistance, points 15
24

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Carbon (C), % 0 to 0.020
0 to 0.010
Chromium (Cr), % 22 to 24
6.0 to 10
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 0 to 1.5
5.0 to 8.0
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 15 to 16.5
21 to 25
Nickel (Ni), % 56.4 to 63
53.9 to 68
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.020
0 to 0.010