Grade CX2MW Nickel vs. SAE-AISI 1035 Steel

Grade CX2MW nickel belongs to the nickel alloys classification, while SAE-AISI 1035 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade CX2MW nickel and the bottom bar is SAE-AISI 1035 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 34
13 to 21
Fatigue Strength, MPa 260
210 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 84
73
Tensile Strength: Ultimate (UTS), MPa 620
570 to 620
Tensile Strength: Yield (Proof), MPa 350
300 to 530

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1550
1460
Melting Onset (Solidus), °C 1490
1420
Specific Heat Capacity, J/kg-K 430
470
Thermal Conductivity, W/m-K 10
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 65
1.8
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 12
1.4
Embodied Energy, MJ/kg 170
18
Embodied Water, L/kg 290
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
79 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 290
250 to 740
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 19
20 to 22
Strength to Weight: Bending, points 18
19 to 21
Thermal Diffusivity, mm2/s 2.7
14
Thermal Shock Resistance, points 17
18 to 20

Alloy Composition

Carbon (C), % 0 to 0.020
0.32 to 0.38
Chromium (Cr), % 20 to 22.5
0
Iron (Fe), % 2.0 to 6.0
98.6 to 99.08
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 12.5 to 14.5
0
Nickel (Ni), % 51.3 to 63
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.8
0
Sulfur (S), % 0 to 0.025
0 to 0.050
Tungsten (W), % 2.5 to 3.5
0
Vanadium (V), % 0 to 0.35
0