Grade CZ100 Nickel vs. N07776 Nickel
Both grade CZ100 nickel and N07776 nickel are nickel alloys. They have 57% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade CZ100 nickel and the bottom bar is N07776 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 11 | |
| 39 |
| Fatigue Strength, MPa | 68 | |
| 220 |
| Poisson's Ratio | 0.31 | |
| 0.3 |
| Shear Modulus, GPa | 69 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 970 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1550 |
| Melting Onset (Solidus), °C | 1300 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 430 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 85 |
| Density, g/cm3 | 8.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 15 |
| Embodied Energy, MJ/kg | 140 | |
| 210 |
| Embodied Water, L/kg | 230 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 54 | |
| 180 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 |
| Strength to Weight: Axial, points | 12 | |
| 22 |
| Strength to Weight: Bending, points | 14 | |
| 20 |
| Thermal Shock Resistance, points | 14 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 2.0 |
| Carbon (C), % | 0 to 1.0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 12 to 22 |
| Copper (Cu), % | 0 to 1.3 | |
| 0 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 to 24.5 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 15 |
| Nickel (Ni), % | 95 to 100 | |
| 50 to 60 |
| Niobium (Nb), % | 0 | |
| 4.0 to 6.0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 2.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 1.0 |
| Tungsten (W), % | 0 | |
| 0.5 to 2.5 |