Grade FDC Steel vs. EN 1.4612 Stainless Steel

Both grade FDC steel and EN 1.4612 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade FDC steel and the bottom bar is EN 1.4612 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 1680
1690 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
790
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
16
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.6
Embodied Energy, MJ/kg 19
50
Embodied Water, L/kg 47
140

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 60
60 to 65
Strength to Weight: Bending, points 40
40 to 43
Thermal Shock Resistance, points 50
58 to 63

Alloy Composition

Aluminum (Al), % 0
1.4 to 1.8
Carbon (C), % 0.6 to 0.75
0 to 0.015
Chromium (Cr), % 0 to 0.3
11 to 12.5
Copper (Cu), % 0 to 0.12
0
Iron (Fe), % 98 to 99.4
71.5 to 75.5
Manganese (Mn), % 0.5 to 1.2
0 to 0.1
Molybdenum (Mo), % 0
1.8 to 2.3
Nickel (Ni), % 0
10.2 to 11.3
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0.1 to 0.35
0 to 0.1
Sulfur (S), % 0 to 0.025
0 to 0.0050
Titanium (Ti), % 0
0.2 to 0.5