Grade FDC Steel vs. EN 1.5521 Steel

Both grade FDC steel and EN 1.5521 steel are iron alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is grade FDC steel and the bottom bar is EN 1.5521 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 510
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Reduction in Area, % 42
59 to 72
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 1680
430 to 1390

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 60
15 to 49
Strength to Weight: Bending, points 40
16 to 35
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 50
13 to 41

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.6 to 0.75
0.16 to 0.2
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.12
0 to 0.25
Iron (Fe), % 98 to 99.4
98 to 98.9
Manganese (Mn), % 0.5 to 1.2
0.9 to 1.2
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.1 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.025