MakeItFrom.com
Menu (ESC)

Grade FDC Steel vs. EN 1.7383 Steel

Both grade FDC steel and EN 1.7383 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade FDC steel and the bottom bar is EN 1.7383 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 510
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
74
Tensile Strength: Ultimate (UTS), MPa 1680
560 to 610

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
460
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
3.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 47
59

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 60
20 to 22
Strength to Weight: Bending, points 40
19 to 20
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 50
16 to 18

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0.6 to 0.75
0.080 to 0.15
Chromium (Cr), % 0 to 0.3
2.0 to 2.5
Copper (Cu), % 0 to 0.12
0 to 0.3
Iron (Fe), % 98 to 99.4
94.3 to 96.6
Manganese (Mn), % 0.5 to 1.2
0.4 to 0.8
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.1 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010