Grade FDC Steel vs. SAE-AISI T1 Steel

Both grade FDC steel and SAE-AISI T1 steel are iron alloys. They have 77% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is grade FDC steel and the bottom bar is SAE-AISI T1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 1680
770 to 2130

Thermal Properties

Latent Heat of Fusion, J/g 250
240
Melting Completion (Liquidus), °C 1450
1810
Melting Onset (Solidus), °C 1410
1750
Specific Heat Capacity, J/kg-K 470
410
Thermal Conductivity, W/m-K 51
20
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
45
Density, g/cm3 7.8
9.3
Embodied Carbon, kg CO2/kg material 1.4
8.2
Embodied Energy, MJ/kg 19
130
Embodied Water, L/kg 47
90

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 60
23 to 64
Strength to Weight: Bending, points 40
20 to 40
Thermal Diffusivity, mm2/s 14
5.2
Thermal Shock Resistance, points 50
23 to 64

Alloy Composition

Carbon (C), % 0.6 to 0.75
0.65 to 0.8
Chromium (Cr), % 0 to 0.3
3.8 to 4.5
Copper (Cu), % 0 to 0.12
0 to 0.25
Iron (Fe), % 98 to 99.4
73.2 to 77.2
Manganese (Mn), % 0.5 to 1.2
0.1 to 0.4
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.1 to 0.35
0.2 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
17.3 to 18.8
Vanadium (V), % 0
0.9 to 1.3