Grade FDC Steel vs. S36200 Stainless Steel

Both grade FDC steel and S36200 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade FDC steel and the bottom bar is S36200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 1680
1180 to 1410

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
820
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
12
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 19
40
Embodied Water, L/kg 47
120

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 60
42 to 50
Strength to Weight: Bending, points 40
32 to 36
Thermal Diffusivity, mm2/s 14
4.3
Thermal Shock Resistance, points 50
40 to 48

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.6 to 0.75
0 to 0.050
Chromium (Cr), % 0 to 0.3
14 to 14.5
Copper (Cu), % 0 to 0.12
0
Iron (Fe), % 98 to 99.4
75.4 to 79.5
Manganese (Mn), % 0.5 to 1.2
0 to 0.5
Molybdenum (Mo), % 0
0 to 0.3
Nickel (Ni), % 0
6.5 to 7.0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.1 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0.6 to 0.9