Grade FDSiCr Steel vs. EN 1.4911 Stainless Steel

Both grade FDSiCr steel and EN 1.4911 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade FDSiCr steel and the bottom bar is EN 1.4911 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 1930
1070

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 410
700
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 48
20
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
20
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 20
49
Embodied Water, L/kg 48
130

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 69
38
Strength to Weight: Bending, points 44
30
Thermal Diffusivity, mm2/s 13
5.4
Thermal Shock Resistance, points 58
37

Alloy Composition

Boron (B), % 0
0.0050 to 0.015
Carbon (C), % 0.5 to 0.6
0.050 to 0.12
Chromium (Cr), % 0.5 to 0.8
9.8 to 11.2
Cobalt (Co), % 0
5.0 to 7.0
Copper (Cu), % 0 to 0.12
0
Iron (Fe), % 96.5 to 97.8
75.7 to 83.8
Manganese (Mn), % 0.5 to 0.9
0.3 to 1.3
Molybdenum (Mo), % 0
0.5 to 1.0
Nickel (Ni), % 0
0.2 to 1.2
Niobium (Nb), % 0
0.2 to 0.5
Nitrogen (N), % 0
0 to 0.035
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 1.2 to 1.6
0.1 to 0.8
Sulfur (S), % 0 to 0.025
0 to 0.015
Tungsten (W), % 0
0 to 0.7
Vanadium (V), % 0
0.1 to 0.4