Grade M30C Nickel vs. AWS E316LMn

Grade M30C nickel belongs to the nickel alloys classification, while AWS E316LMn belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade M30C nickel and the bottom bar is AWS E316LMn.

Grade M30C (J24130) Cast Nickel AWS E316LMn (W31622) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		160
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		29
Elongation at Break, %		23

Poisson's Ratio		0.32
Poisson's Ratio		0.28

Shear Modulus, GPa		61
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		510
Tensile Strength: Ultimate (UTS), MPa		620

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1290
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		1240
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		60
Base Metal Price, % relative		24

Density, g/cm³		8.8
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		9.5
Embodied Carbon, kg CO₂/kg material		4.6

Embodied Energy, MJ/kg		140
Embodied Energy, MJ/kg		64

Embodied Water, L/kg		250
Embodied Water, L/kg		180

Common Calculations

Stiffness to Weight: Axial, points		10
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		21
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		16
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		15

Alloy Composition

Carbon (C), %		0 to 0.3
Carbon (C), %		0 to 0.040

Chromium (Cr), %		0
Chromium (Cr), %		18 to 21

Copper (Cu), %		26 to 33
Copper (Cu), %		0 to 0.75

Iron (Fe), %		0 to 3.5
Iron (Fe), %		47.5 to 59.4

Manganese (Mn), %		0 to 1.5
Manganese (Mn), %		5.0 to 8.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		2.5 to 3.5

Nickel (Ni), %		56.6 to 72
Nickel (Ni), %		15 to 18

Niobium (Nb), %		1.0 to 3.0
Niobium (Nb), %		0

Nitrogen (N), %		0
Nitrogen (N), %		0.1 to 0.25

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		1.0 to 2.0
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030