Grade M30H Nickel vs. Solder Alloy 141

Grade M30H nickel belongs to the nickel alloys classification, while solder alloy 141 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is grade M30H nickel and the bottom bar is solder alloy 141.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 160
37
Elongation at Break, % 11
39
Poisson's Ratio 0.32
0.39
Shear Modulus, GPa 61
13
Tensile Strength: Ultimate (UTS), MPa 770
54

Thermal Properties

Latent Heat of Fusion, J/g 320
46
Melting Completion (Liquidus), °C 1250
190
Melting Onset (Solidus), °C 1200
180
Specific Heat Capacity, J/kg-K 440
180
Thermal Conductivity, W/m-K 22
48
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
10

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.9
Embodied Carbon, kg CO2/kg material 7.7
11
Embodied Energy, MJ/kg 110
180
Embodied Water, L/kg 250
970

Common Calculations

Stiffness to Weight: Axial, points 10
2.3
Stiffness to Weight: Bending, points 21
13
Strength to Weight: Axial, points 25
1.7
Strength to Weight: Bending, points 22
3.6
Thermal Diffusivity, mm2/s 5.7
29
Thermal Shock Resistance, points 27
4.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
2.0 to 3.0
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.3
0
Copper (Cu), % 27 to 33
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 3.5
0 to 0.020
Lead (Pb), % 0
35.9 to 38.5
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 57.9 to 70.3
0 to 0.010
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 2.7 to 3.7
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
59.5 to 60.5
Zinc (Zn), % 0
0 to 0.0010