Grade N12MV Nickel vs. C72200 Copper-nickel
Grade N12MV nickel belongs to the nickel alloys classification, while C72200 copper-nickel belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade N12MV nickel and the bottom bar is C72200 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 130 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 84 | |
| 48 |
| Tensile Strength: Ultimate (UTS), MPa | 600 | |
| 350 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 230 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1180 |
| Melting Onset (Solidus), °C | 1570 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Expansion, µm/m-K | 10 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 36 |
| Density, g/cm3 | 9.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 16 | |
| 3.9 |
| Embodied Energy, MJ/kg | 200 | |
| 59 |
| Embodied Water, L/kg | 260 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 8.0 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 17 | |
| 12 to 17 |
| Thermal Shock Resistance, points | 19 | |
| 12 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 0 to 1.0 | |
| 0.3 to 0.7 |
| Copper (Cu), % | 0 | |
| 78.1 to 84.2 |
| Iron (Fe), % | 4.0 to 6.0 | |
| 0.5 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 26 to 30 | |
| 0 |
| Nickel (Ni), % | 60.2 to 69.8 | |
| 15 to 18 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.2 |