Grade N7M Nickel vs. SAE-AISI 1019 Steel

Grade N7M nickel belongs to the nickel alloys classification, while SAE-AISI 1019 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is grade N7M nickel and the bottom bar is SAE-AISI 1019 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 22
17 to 29
Fatigue Strength, MPa 190
190 to 290
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 85
73
Tensile Strength: Ultimate (UTS), MPa 590
470 to 520
Tensile Strength: Yield (Proof), MPa 310
250 to 430

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1650
1460
Melting Onset (Solidus), °C 1590
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Expansion, µm/m-K 9.9
12

Otherwise Unclassified Properties

Base Metal Price, % relative 75
1.8
Density, g/cm3 9.3
7.9
Embodied Carbon, kg CO2/kg material 16
1.4
Embodied Energy, MJ/kg 200
18
Embodied Water, L/kg 270
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
82 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 220
160 to 500
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 18
17 to 18
Strength to Weight: Bending, points 17
17 to 18
Thermal Shock Resistance, points 19
15 to 16

Alloy Composition

Carbon (C), % 0 to 0.070
0.15 to 0.2
Chromium (Cr), % 0 to 1.0
0
Iron (Fe), % 0 to 3.0
98.7 to 99.15
Manganese (Mn), % 0 to 1.0
0.7 to 1.0
Molybdenum (Mo), % 30 to 33
0
Nickel (Ni), % 60.9 to 70
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050