Grade N7M Nickel vs. SAE-AISI 1151 Steel
Grade N7M nickel belongs to the nickel alloys classification, while SAE-AISI 1151 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade N7M nickel and the bottom bar is SAE-AISI 1151 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 22 | |
| 11 to 17 |
| Fatigue Strength, MPa | 190 | |
| 260 to 410 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 85 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 710 to 800 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 390 to 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 400 |
| Melting Completion (Liquidus), °C | 1650 | |
| 1460 |
| Melting Onset (Solidus), °C | 1590 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 1.8 |
| Density, g/cm3 | 9.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 16 | |
| 1.4 |
| Embodied Energy, MJ/kg | 200 | |
| 18 |
| Embodied Water, L/kg | 270 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 86 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 400 to 1170 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 17 | |
| 22 to 24 |
| Thermal Shock Resistance, points | 19 | |
| 22 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0.48 to 0.55 |
| Chromium (Cr), % | 0 to 1.0 | |
| 0 |
| Iron (Fe), % | 0 to 3.0 | |
| 98.3 to 98.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 30 to 33 | |
| 0 |
| Nickel (Ni), % | 60.9 to 70 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0.080 to 0.13 |