Grade N7M Nickel vs. S35000 Stainless Steel
Grade N7M nickel belongs to the nickel alloys classification, while S35000 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade N7M nickel and the bottom bar is S35000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 22 | |
| 2.3 to 14 |
| Fatigue Strength, MPa | 190 | |
| 380 to 520 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 85 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 1300 to 1570 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 660 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 900 |
| Melting Completion (Liquidus), °C | 1650 | |
| 1460 |
| Melting Onset (Solidus), °C | 1590 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 14 |
| Density, g/cm3 | 9.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 16 | |
| 3.2 |
| Embodied Energy, MJ/kg | 200 | |
| 44 |
| Embodied Water, L/kg | 270 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 28 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 1070 to 3360 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 18 | |
| 46 to 56 |
| Strength to Weight: Bending, points | 17 | |
| 34 to 38 |
| Thermal Shock Resistance, points | 19 | |
| 42 to 51 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 0 to 1.0 | |
| 16 to 17 |
| Iron (Fe), % | 0 to 3.0 | |
| 72.7 to 76.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 30 to 33 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 60.9 to 70 | |
| 4.0 to 5.0 |
| Nitrogen (N), % | 0 | |
| 0.070 to 0.13 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |