Grade TDC Steel vs. EN 1.5514 Steel

Both grade TDC steel and EN 1.5514 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is grade TDC steel and the bottom bar is EN 1.5514 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 510
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Reduction in Area, % 50
64 to 69
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 1700
470 to 1680

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 60
17 to 60
Strength to Weight: Bending, points 40
17 to 40
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 50
14 to 50

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.6 to 0.75
0.3 to 0.35
Chromium (Cr), % 0 to 0.3
0 to 0.3
Copper (Cu), % 0 to 0.1
0 to 0.25
Iron (Fe), % 98 to 99.4
97.8 to 99.099
Manganese (Mn), % 0.5 to 1.2
0.6 to 0.9
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.1 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.020
0 to 0.025