Grade Ti-Pd17 Titanium vs. R58150 Titanium
Both grade Ti-Pd17 titanium and R58150 titanium are titanium alloys. They have 85% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade Ti-Pd17 titanium and the bottom bar is R58150 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 140 |
| Elongation at Break, % | 22 | |
| 13 |
| Fatigue Strength, MPa | 140 | |
| 330 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 320 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1760 |
| Melting Onset (Solidus), °C | 1610 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 500 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 8.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 5.4 |
| Embodied Carbon, kg CO2/kg material | 36 | |
| 31 |
| Embodied Energy, MJ/kg | 600 | |
| 480 |
| Embodied Water, L/kg | 230 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 | |
| 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 1110 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 32 |
| Strength to Weight: Axial, points | 17 | |
| 40 |
| Strength to Weight: Bending, points | 21 | |
| 35 |
| Thermal Shock Resistance, points | 21 | |
| 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.1 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 14 to 16 |
| Nickel (Ni), % | 0 to 0.030 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 to 0.2 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Titanium (Ti), % | 98.9 to 99.96 | |
| 83.5 to 86 |
| Residuals, % | 0 to 0.4 | |
| 0 |