Grade Ti-Pd8A Titanium vs. 5457 Aluminum

Grade Ti-Pd8A titanium belongs to the titanium alloys classification, while 5457 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade Ti-Pd8A titanium and the bottom bar is 5457 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
32 to 55
Elastic (Young's, Tensile) Modulus, GPa 110
68
Elongation at Break, % 13
6.0 to 22
Fatigue Strength, MPa 260
55 to 98
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 40
26
Tensile Strength: Ultimate (UTS), MPa 500
130 to 210
Tensile Strength: Yield (Proof), MPa 430
50 to 190

Thermal Properties

Latent Heat of Fusion, J/g 420
400
Maximum Temperature: Mechanical, °C 320
180
Melting Completion (Liquidus), °C 1660
660
Melting Onset (Solidus), °C 1610
630
Specific Heat Capacity, J/kg-K 540
900
Thermal Conductivity, W/m-K 21
180
Thermal Expansion, µm/m-K 8.7
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.5
46
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
150

Otherwise Unclassified Properties

Density, g/cm3 4.5
2.7
Embodied Carbon, kg CO2/kg material 49
8.4
Embodied Energy, MJ/kg 840
160
Embodied Water, L/kg 520
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 65
12 to 23
Resilience: Unit (Modulus of Resilience), kJ/m3 880
18 to 250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
50
Strength to Weight: Axial, points 31
13 to 21
Strength to Weight: Bending, points 31
21 to 28
Thermal Diffusivity, mm2/s 8.6
72
Thermal Shock Resistance, points 39
5.7 to 9.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
97.8 to 99.05
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.2
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
0 to 0.1
Magnesium (Mg), % 0
0.8 to 1.2
Manganese (Mn), % 0
0.15 to 0.45
Nickel (Ni), % 0 to 0.050
0
Oxygen (O), % 0 to 0.4
0
Palladium (Pd), % 0.12 to 0.3
0
Silicon (Si), % 0
0 to 0.080
Titanium (Ti), % 98.8 to 99.9
0
Vanadium (V), % 0
0 to 0.050
Zinc (Zn), % 0
0 to 0.050
Residuals, % 0 to 0.4
0 to 0.1