Grade Ti-Pd8A Titanium vs. AWS BNi-11
Grade Ti-Pd8A titanium belongs to the titanium alloys classification, while AWS BNi-11 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade Ti-Pd8A titanium and the bottom bar is AWS BNi-11.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Poisson's Ratio | 0.32 | |
| 0.3 |
| Shear Modulus, GPa | 40 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 340 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1100 |
| Melting Onset (Solidus), °C | 1610 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 450 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 11 |
| Embodied Energy, MJ/kg | 840 | |
| 160 |
| Embodied Water, L/kg | 520 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 35 | |
| 21 |
| Strength to Weight: Axial, points | 31 | |
| 18 |
| Strength to Weight: Bending, points | 31 | |
| 17 |
| Thermal Shock Resistance, points | 39 | |
| 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Boron (B), % | 0 | |
| 2.2 to 3.1 |
| Carbon (C), % | 0 to 0.1 | |
| 0.3 to 0.5 |
| Chromium (Cr), % | 0 | |
| 9.0 to 11.8 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 2.5 to 4.0 |
| Nickel (Ni), % | 0 to 0.050 | |
| 62.9 to 71.2 |
| Oxygen (O), % | 0 to 0.4 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 | |
| 3.4 to 4.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 98.8 to 99.9 | |
| 0 to 0.050 |
| Tungsten (W), % | 0 | |
| 11.5 to 12.8 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |