Grade Ti-Pd8A Titanium vs. EN AC-51500 Aluminum

Grade Ti-Pd8A titanium belongs to the titanium alloys classification, while EN AC-51500 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is grade Ti-Pd8A titanium and the bottom bar is EN AC-51500 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
80
Elastic (Young's, Tensile) Modulus, GPa 110
68
Elongation at Break, % 13
5.6
Fatigue Strength, MPa 260
120
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 40
26
Tensile Strength: Ultimate (UTS), MPa 500
280
Tensile Strength: Yield (Proof), MPa 430
160

Thermal Properties

Latent Heat of Fusion, J/g 420
430
Maximum Temperature: Mechanical, °C 320
170
Melting Completion (Liquidus), °C 1660
630
Melting Onset (Solidus), °C 1610
590
Specific Heat Capacity, J/kg-K 540
910
Thermal Conductivity, W/m-K 21
120
Thermal Expansion, µm/m-K 8.7
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.5
26
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
88

Otherwise Unclassified Properties

Density, g/cm3 4.5
2.6
Embodied Carbon, kg CO2/kg material 49
9.0
Embodied Energy, MJ/kg 840
150
Embodied Water, L/kg 520
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 65
13
Resilience: Unit (Modulus of Resilience), kJ/m3 880
190
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
52
Strength to Weight: Axial, points 31
29
Strength to Weight: Bending, points 31
36
Thermal Diffusivity, mm2/s 8.6
49
Thermal Shock Resistance, points 39
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
89.8 to 93.1
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.050
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
0 to 0.25
Magnesium (Mg), % 0
4.7 to 6.0
Manganese (Mn), % 0
0.4 to 0.8
Nickel (Ni), % 0 to 0.050
0
Oxygen (O), % 0 to 0.4
0
Palladium (Pd), % 0.12 to 0.3
0
Silicon (Si), % 0
1.8 to 2.6
Titanium (Ti), % 98.8 to 99.9
0 to 0.25
Zinc (Zn), % 0
0 to 0.070
Residuals, % 0 to 0.4
0 to 0.15