MakeItFrom.com
Menu (ESC)

Grade Ti-Pd8A Titanium vs. Grade 13 Titanium

Both grade Ti-Pd8A titanium and grade 13 titanium are titanium alloys. Their average alloy composition is basically identical. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade Ti-Pd8A titanium and the bottom bar is grade 13 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 13
27
Fatigue Strength, MPa 260
140
Poisson's Ratio 0.32
0.32
Shear Modulus, GPa 40
41
Tensile Strength: Ultimate (UTS), MPa 500
310
Tensile Strength: Yield (Proof), MPa 430
190

Thermal Properties

Latent Heat of Fusion, J/g 420
420
Maximum Temperature: Mechanical, °C 320
320
Melting Completion (Liquidus), °C 1660
1660
Melting Onset (Solidus), °C 1610
1610
Specific Heat Capacity, J/kg-K 540
540
Thermal Conductivity, W/m-K 21
22
Thermal Expansion, µm/m-K 8.7
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.5
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
7.2

Otherwise Unclassified Properties

Density, g/cm3 4.5
4.5
Embodied Carbon, kg CO2/kg material 49
32
Embodied Energy, MJ/kg 840
520
Embodied Water, L/kg 520
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 65
73
Resilience: Unit (Modulus of Resilience), kJ/m3 880
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 35
35
Strength to Weight: Axial, points 31
19
Strength to Weight: Bending, points 31
22
Thermal Diffusivity, mm2/s 8.6
8.9
Thermal Shock Resistance, points 39
24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.1
0 to 0.080
Hydrogen (H), % 0 to 0.015
0 to 0.015
Iron (Fe), % 0 to 0.25
0 to 0.2
Nickel (Ni), % 0 to 0.050
0.4 to 0.6
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0 to 0.4
0 to 0.1
Palladium (Pd), % 0.12 to 0.3
0
Ruthenium (Ru), % 0
0.040 to 0.060
Titanium (Ti), % 98.8 to 99.9
98.5 to 99.56
Residuals, % 0 to 0.4
0 to 0.4