Grade VDC Steel vs. EN 1.4887 Stainless Steel

Both grade VDC steel and EN 1.4887 stainless steel are iron alloys. They have 41% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade VDC steel and the bottom bar is EN 1.4887 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 510
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 1700
580

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1410
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
39
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
6.7
Embodied Energy, MJ/kg 19
96
Embodied Water, L/kg 47
210

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 60
20
Strength to Weight: Bending, points 40
19
Thermal Diffusivity, mm2/s 14
3.2
Thermal Shock Resistance, points 50
14

Alloy Composition

Carbon (C), % 0.6 to 0.75
0 to 0.15
Chromium (Cr), % 0 to 0.3
20 to 23
Copper (Cu), % 0 to 0.060
0
Iron (Fe), % 98.3 to 99.35
34.2 to 45
Manganese (Mn), % 0.5 to 1.0
0 to 2.0
Nickel (Ni), % 0
33 to 37
Niobium (Nb), % 0
1.0 to 1.5
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0.15 to 0.3
1.0 to 2.0
Sulfur (S), % 0 to 0.020
0 to 0.015