Grade VDCrV Steel vs. EN 1.7221 Steel

Both grade VDCrV steel and EN 1.7221 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is grade VDCrV steel and the bottom bar is EN 1.7221 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 520
200 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 1730
650 to 780

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.5
Embodied Energy, MJ/kg 26
20
Embodied Water, L/kg 49
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 61
23 to 27
Strength to Weight: Bending, points 41
21 to 24
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 51
19 to 23

Alloy Composition

Carbon (C), % 0.62 to 0.72
0.22 to 0.29
Chromium (Cr), % 0.4 to 0.6
0.8 to 1.2
Copper (Cu), % 0 to 0.060
0
Iron (Fe), % 97.8 to 98.8
96.8 to 98.3
Manganese (Mn), % 0.5 to 0.9
0.5 to 0.8
Molybdenum (Mo), % 0
0.15 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.15 to 0.3
0 to 0.6
Sulfur (S), % 0 to 0.020
0 to 0.030
Vanadium (V), % 0.15 to 0.25
0