Graphite vs. SiAlON
Both graphite and SiAlON are non-oxide engineering ceramics. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is graphite and the bottom bar is SiAlON.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 90 | |
| 2620 |
| Elastic (Young's, Tensile) Modulus, GPa | 21 | |
| 290 |
| Flexural Strength, MPa | 80 | |
| 680 |
| Tensile Strength: Ultimate (UTS), MPa | 18 | |
| 190 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 220 | |
| 1200 |
| Thermal Conductivity, W/m-K | 6.0 | |
| 19 |
| Thermal Expansion, µm/m-K | 4.9 | |
| 3.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 3.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.7 | |
| 50 |
| Stiffness to Weight: Bending, points | 53 | |
| 67 |
| Strength to Weight: Axial, points | 2.9 | |
| 16 |
| Strength to Weight: Bending, points | 8.7 | |
| 22 |
| Thermal Shock Resistance, points | 12 | |
| 13 |