Graphite vs. Zircon

Graphite belongs to the non-oxide engineering ceramics classification, while zircon belongs to the oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is graphite and the bottom bar is zircon.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 1.8
3.9
Flexural Strength, MPa 80
450
Maximum Temperature: Mechanical, °C 220
1650
Strength to Weight: Axial, points 2.9
21
Strength to Weight: Bending, points 8.7
25
Tensile Strength: Ultimate (UTS), MPa 18
290
Thermal Conductivity, W/m-K 6.0
3.5
Thermal Expansion, µm/m-K 4.9
5.0