MakeItFrom.com
Menu (ESC)

Grey Cast Iron vs. AWS ENiCrMo-4

Grey cast iron belongs to the iron alloys classification, while AWS ENiCrMo-4 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grey cast iron and the bottom bar is AWS ENiCrMo-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
220
Elongation at Break, % 9.6
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 69
84
Tensile Strength: Ultimate (UTS), MPa 160 to 450
790

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Melting Completion (Liquidus), °C 1380
1590
Melting Onset (Solidus), °C 1180
1530
Specific Heat Capacity, J/kg-K 490
410
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
70
Density, g/cm3 7.5
9.0
Embodied Carbon, kg CO2/kg material 1.5
13
Embodied Energy, MJ/kg 21
170
Embodied Water, L/kg 44
280

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 5.8 to 17
24
Strength to Weight: Bending, points 8.7 to 17
21
Thermal Shock Resistance, points 6.0 to 17
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 3.1 to 3.4
0 to 0.020
Chromium (Cr), % 0
14.5 to 16.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 92.1 to 93.9
4.0 to 7.0
Manganese (Mn), % 0.5 to 0.7
0 to 1.0
Molybdenum (Mo), % 0
15 to 17
Nickel (Ni), % 0
49.9 to 63.5
Phosphorus (P), % 0 to 0.9
0 to 0.040
Silicon (Si), % 2.5 to 2.8
0 to 0.2
Sulfur (S), % 0 to 0.15
0 to 0.030
Tungsten (W), % 0
3.0 to 4.5
Vanadium (V), % 0
0 to 0.35
Residuals, % 0
0 to 0.5