Grey Cast Iron vs. Grade 366 Molybdenum
Grey cast iron belongs to the iron alloys classification, while grade 366 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grey cast iron and the bottom bar is grade 366 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 300 |
| Elongation at Break, % | 9.6 | |
| 2.2 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 69 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 450 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 98 to 290 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 210 |
| Thermal Expansion, µm/m-K | 11 | |
| 7.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.5 | |
| 12 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 27 |
| Embodied Energy, MJ/kg | 21 | |
| 340 |
| Embodied Water, L/kg | 44 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 37 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 27 to 240 | |
| 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 5.8 to 17 | |
| 13 |
| Strength to Weight: Bending, points | 8.7 to 17 | |
| 13 |
| Thermal Shock Resistance, points | 6.0 to 17 | |
| 18 |
Alloy Composition
| Carbon (C), % | 3.1 to 3.4 | |
| 0 to 0.030 |
| Iron (Fe), % | 92.1 to 93.9 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.5 to 0.7 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 66.9 to 73 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0025 |
| Phosphorus (P), % | 0 to 0.9 | |
| 0 |
| Silicon (Si), % | 2.5 to 2.8 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.15 | |
| 0 |
| Tungsten (W), % | 0 | |
| 27 to 33 |