Grey Cast Iron vs. C84000 Brass
Grey cast iron belongs to the iron alloys classification, while C84000 brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is grey cast iron and the bottom bar is C84000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 300 | |
| 65 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 110 |
| Elongation at Break, % | 9.6 | |
| 27 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 69 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 450 | |
| 250 |
| Tensile Strength: Yield (Proof), MPa | 98 to 290 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 190 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1040 |
| Melting Onset (Solidus), °C | 1180 | |
| 940 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 380 |
| Thermal Conductivity, W/m-K | 46 | |
| 72 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 16 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 30 |
| Density, g/cm3 | 7.5 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.0 |
| Embodied Energy, MJ/kg | 21 | |
| 49 |
| Embodied Water, L/kg | 44 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 37 | |
| 58 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 27 to 240 | |
| 83 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 5.8 to 17 | |
| 8.2 |
| Strength to Weight: Bending, points | 8.7 to 17 | |
| 10 |
| Thermal Diffusivity, mm2/s | 13 | |
| 22 |
| Thermal Shock Resistance, points | 6.0 to 17 | |
| 9.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 3.1 to 3.4 | |
| 0 |
| Copper (Cu), % | 0 | |
| 82 to 89 |
| Iron (Fe), % | 92.1 to 93.9 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 | |
| 0 to 0.090 |
| Manganese (Mn), % | 0.5 to 0.7 | |
| 0 to 0.010 |
| Nickel (Ni), % | 0 | |
| 0.5 to 2.0 |
| Phosphorus (P), % | 0 to 0.9 | |
| 0 to 0.050 |
| Silicon (Si), % | 2.5 to 2.8 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.15 | |
| 0.1 to 0.65 |
| Tin (Sn), % | 0 | |
| 2.0 to 4.0 |
| Zinc (Zn), % | 0 | |
| 5.0 to 14 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.7 |