Grey Cast Iron vs. C99600 Bronze
Grey cast iron belongs to the iron alloys classification, while C99600 bronze belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grey cast iron and the bottom bar is C99600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 150 |
| Elongation at Break, % | 9.6 | |
| 27 to 34 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 69 | |
| 56 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 450 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 98 to 290 | |
| 250 to 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 240 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1100 |
| Melting Onset (Solidus), °C | 1180 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 440 |
| Thermal Expansion, µm/m-K | 11 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 22 |
| Density, g/cm3 | 7.5 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.2 |
| Embodied Energy, MJ/kg | 21 | |
| 51 |
| Embodied Water, L/kg | 44 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 37 | |
| 130 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 27 to 240 | |
| 210 to 310 |
| Stiffness to Weight: Axial, points | 13 | |
| 10 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 5.8 to 17 | |
| 19 |
| Strength to Weight: Bending, points | 8.7 to 17 | |
| 19 |
| Thermal Shock Resistance, points | 6.0 to 17 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 1.0 to 2.8 |
| Carbon (C), % | 3.1 to 3.4 | |
| 0 to 0.050 |
| Cobalt (Co), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 | |
| 50.8 to 60 |
| Iron (Fe), % | 92.1 to 93.9 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.5 to 0.7 | |
| 39 to 45 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.9 | |
| 0 |
| Silicon (Si), % | 2.5 to 2.8 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.15 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.3 |