H02 C47940 Brass vs. H02 C74000 Nickel Silver
Both H02 C47940 brass and H02 C74000 nickel silver are copper alloys. Both are furnished in the H02 (half hard) temper. They have 83% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is H02 C47940 brass and the bottom bar is H02 C74000 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 180 |
| Melting Completion (Liquidus), °C | 850 | |
| 990 |
| Melting Onset (Solidus), °C | 800 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 30 |
| Density, g/cm3 | 8.2 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.4 |
| Embodied Energy, MJ/kg | 47 | |
| 54 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 14 | |
| 16 |
| Strength to Weight: Bending, points | 15 | |
| 16 |
| Thermal Shock Resistance, points | 14 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 63 to 66 | |
| 69 to 73.5 |
| Iron (Fe), % | 0.1 to 1.0 | |
| 0 to 0.25 |
| Lead (Pb), % | 1.0 to 2.0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0.1 to 0.5 | |
| 9.0 to 11 |
| Tin (Sn), % | 1.2 to 2.0 | |
| 0 |
| Zinc (Zn), % | 28.1 to 34.6 | |
| 14.2 to 22 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |