Half-hard K93600 vs. Half-hard K93050 Alloy
Both half-hard K93600 and half-hard K93050 alloy are iron alloys. Both are furnished in the half-hard temper. There are 11 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is half-hard K93600 and the bottom bar is half-hard K93050 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Tensile Strength: Ultimate (UTS), MPa | 650 | |
680 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
1380 |
Specific Heat Capacity, J/kg-K | 520 | |
460 |
Thermal Expansion, µm/m-K | 7.3 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
8.2 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
23 |
Strength to Weight: Axial, points | 22 | |
23 |
Strength to Weight: Bending, points | 21 | |
21 |
Thermal Shock Resistance, points | 47 | |
21 |