Hardened SAE-AISI F1 vs. Hardened SAE-AISI H10
Both hardened SAE-AISI F1 and hardened SAE-AISI H10 are iron alloys. Both are furnished in the hardened (H) condition. They have a moderately high 92% of their average alloy composition in common.
For each property being compared, the top bar is hardened SAE-AISI F1 and the bottom bar is hardened SAE-AISI H10.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Rockwell C Hardness | 72 | |
| 63 |
| Shear Modulus, GPa | 72 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 2320 | |
| 2030 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1470 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 38 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 9.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 6.5 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 3.4 |
| Embodied Energy, MJ/kg | 24 | |
| 48 |
| Embodied Water, L/kg | 46 | |
| 71 |
Common Calculations
| PREN (Pitting Resistance) | 2.3 | |
| 12 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 82 | |
| 72 |
| Strength to Weight: Bending, points | 49 | |
| 46 |
| Thermal Diffusivity, mm2/s | 12 | |
| 10 |
| Thermal Shock Resistance, points | 70 | |
| 66 |
Alloy Composition
| Carbon (C), % | 1.0 to 1.3 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 0 | |
| 3.0 to 3.8 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 95.9 to 98 | |
| 89.5 to 93.4 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.25 to 0.7 |
| Molybdenum (Mo), % | 0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.1 to 0.5 | |
| 0.8 to 1.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 1.0 to 1.8 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.75 |