Hardened SAE-AISI T8 vs. Hardened AISI W5
Both hardened SAE-AISI T8 and hardened AISI W5 are iron alloys. Both are furnished in the hardened (H) condition. They have 75% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is hardened SAE-AISI T8 and the bottom bar is hardened AISI W5.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Rockwell C Hardness | 66 | |
| 73 |
| Shear Modulus, GPa | 78 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 2140 | |
| 2360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Melting Completion (Liquidus), °C | 1730 | |
| 1450 |
| Melting Onset (Solidus), °C | 1670 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 470 |
| Thermal Conductivity, W/m-K | 18 | |
| 45 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 2.3 |
| Density, g/cm3 | 9.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 1.6 |
| Embodied Energy, MJ/kg | 160 | |
| 21 |
| Embodied Water, L/kg | 120 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 66 | |
| 84 |
| Strength to Weight: Bending, points | 41 | |
| 50 |
| Thermal Diffusivity, mm2/s | 4.8 | |
| 12 |
| Thermal Shock Resistance, points | 66 | |
| 78 |
Alloy Composition
| Carbon (C), % | 0.75 to 0.85 | |
| 1.1 to 1.2 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0.4 to 0.6 |
| Cobalt (Co), % | 4.3 to 5.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.2 |
| Iron (Fe), % | 69.3 to 75.4 | |
| 96.6 to 98.4 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0.1 to 0.4 |
| Molybdenum (Mo), % | 0.4 to 1.0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 13.3 to 14.8 | |
| 0 to 0.15 |
| Vanadium (V), % | 1.8 to 2.4 | |
| 0 to 0.1 |