Hexagonal Boron Nitride vs. Borosilicate Glass
Hexagonal boron nitride belongs to the non-oxide engineering ceramics classification, while borosilicate glass belongs to the glass and glass-ceramics. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is hexagonal boron nitride and the bottom bar is borosilicate glass.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 21 to 250 | |
| 2000 |
| Elastic (Young's, Tensile) Modulus, GPa | 14 to 60 | |
| 67 to 80 |
| Flexural Strength, MPa | 18 to 140 | |
| 34 to 69 |
| Poisson's Ratio | 0.11 | |
| 0.21 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1030 to 2350 | |
| 360 |
| Specific Heat Capacity, J/kg-K | 840 to 1610 | |
| 830 |
| Thermal Conductivity, W/m-K | 29 to 96 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 0.54 to 18 | |
| 3.3 to 5.1 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 4.0 to 4.4 | |
| 5.4 |
| Dielectric Strength (Breakdown Potential), kV/mm | 61 to 200 | |
| 5.0 to 34 |
| Electrical Dissipation At 1 Hz | 0.0017 | |
| 0.0026 to 0.018 |
| Electrical Dissipation At 1 MHz | 0.00075 to 0.0018 | |
| 0.0017 to 0.0088 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 to 15 | |
| 9.0 to 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.9 to 2.1 | |
| 2.2 to 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 to 18 | |
| 15 to 17 |
| Stiffness to Weight: Bending, points | 42 to 69 | |
| 55 to 61 |
| Thermal Diffusivity, mm2/s | 9.9 to 34 | |
| 0.54 to 0.63 |