High-alumina Refractory vs. Forsterite
Both high-alumina refractory and forsterite are oxide-based engineering ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is high-alumina refractory and the bottom bar is forsterite.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.1 | |
| 2.1 to 3.1 |
| Flexural Strength, MPa | 28 | |
| 40 to 160 |
| Specific Heat Capacity, J/kg-K | 800 | |
| 850 |
| Thermal Conductivity, W/m-K | 1.5 | |
| 1.7 to 3.5 |
| Thermal Diffusivity, mm2/s | 0.87 | |
| 0.94 to 1.3 |
| Thermal Expansion, µm/m-K | 4.3 | |
| 9.0 to 10 |