R31538 Cobalt vs. 5026 Aluminum

R31538 cobalt belongs to the cobalt alloys classification, while 5026 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is 5026 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
70
Elongation at Break, % 13 to 23
5.1 to 11
Fatigue Strength, MPa 310 to 480
94 to 140
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 86
26
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
260 to 320
Tensile Strength: Yield (Proof), MPa 580 to 930
120 to 250

Thermal Properties

Latent Heat of Fusion, J/g 320
400
Melting Completion (Liquidus), °C 1360
650
Melting Onset (Solidus), °C 1290
510
Specific Heat Capacity, J/kg-K 450
890
Thermal Conductivity, W/m-K 13
130
Thermal Expansion, µm/m-K 13
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
31
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
99

Otherwise Unclassified Properties

Density, g/cm3 8.4
2.8
Embodied Carbon, kg CO2/kg material 8.1
8.9
Embodied Energy, MJ/kg 110
150
Embodied Water, L/kg 530
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
15 to 29
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
100 to 440
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
49
Strength to Weight: Axial, points 34 to 45
26 to 32
Strength to Weight: Bending, points 27 to 32
33 to 37
Thermal Diffusivity, mm2/s 3.5
52
Thermal Shock Resistance, points 25 to 33
11 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
88.2 to 94.7
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0 to 0.3
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 0 to 0.75
0.2 to 1.0
Magnesium (Mg), % 0
3.9 to 4.9
Manganese (Mn), % 0 to 1.0
0.6 to 1.8
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Silicon (Si), % 0 to 1.0
0.55 to 1.4
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 1.0
Zirconium (Zr), % 0
0 to 0.3
Residuals, % 0
0 to 0.15

Comparable Variants