MakeItFrom.com
Menu (ESC)

R31538 Cobalt vs. A413.0 Aluminum

R31538 cobalt belongs to the cobalt alloys classification, while A413.0 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is A413.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
73
Elongation at Break, % 13 to 23
3.5
Fatigue Strength, MPa 310 to 480
130
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 86
27
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
240
Tensile Strength: Yield (Proof), MPa 580 to 930
130

Thermal Properties

Latent Heat of Fusion, J/g 320
570
Melting Completion (Liquidus), °C 1360
590
Melting Onset (Solidus), °C 1290
580
Specific Heat Capacity, J/kg-K 450
900
Thermal Conductivity, W/m-K 13
120
Thermal Expansion, µm/m-K 13
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
31
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
110

Otherwise Unclassified Properties

Density, g/cm3 8.4
2.6
Embodied Carbon, kg CO2/kg material 8.1
7.6
Embodied Energy, MJ/kg 110
140
Embodied Water, L/kg 530
1040

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
7.1
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
120
Stiffness to Weight: Axial, points 15
16
Stiffness to Weight: Bending, points 24
54
Strength to Weight: Axial, points 34 to 45
25
Strength to Weight: Bending, points 27 to 32
33
Thermal Diffusivity, mm2/s 3.5
52
Thermal Shock Resistance, points 25 to 33
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
82.9 to 89
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 0 to 0.75
0 to 1.3
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0 to 1.0
0 to 0.35
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0 to 0.5
Nitrogen (N), % 0 to 0.25
0
Silicon (Si), % 0 to 1.0
11 to 13
Tin (Sn), % 0
0 to 0.15
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.25