R31538 Cobalt vs. AWS ER80S-Ni1

R31538 cobalt belongs to the cobalt alloys classification, while AWS ER80S-Ni1 belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is AWS ER80S-Ni1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 23
27
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
72
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
630
Tensile Strength: Yield (Proof), MPa 580 to 930
530

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Melting Completion (Liquidus), °C 1360
1450
Melting Onset (Solidus), °C 1290
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.6

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.1
1.6
Embodied Energy, MJ/kg 110
21
Embodied Water, L/kg 530
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
160
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
740
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
22
Strength to Weight: Bending, points 27 to 32
21
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 25 to 33
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.15 to 0.35
0 to 0.12
Chromium (Cr), % 26 to 30
0 to 0.15
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 0 to 0.75
95.3 to 98.8
Manganese (Mn), % 0 to 1.0
0 to 1.3
Molybdenum (Mo), % 5.0 to 7.0
0 to 0.35
Nickel (Ni), % 0 to 1.0
0.8 to 1.1
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0.4 to 0.8
Sulfur (S), % 0
0 to 0.025
Vanadium (V), % 0
0 to 0.050
Residuals, % 0
0 to 0.5