R31538 Cobalt vs. EN 1.0214 Steel

R31538 cobalt belongs to the cobalt alloys classification, while EN 1.0214 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is EN 1.0214 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 23
12 to 31
Fatigue Strength, MPa 310 to 480
160 to 250
Poisson's Ratio 0.29
0.29
Reduction in Area, % 13 to 22
66 to 80
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
330 to 460
Tensile Strength: Yield (Proof), MPa 580 to 930
210 to 360

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1470
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
7.9

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 8.1
1.4
Embodied Energy, MJ/kg 110
18
Embodied Water, L/kg 530
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
34 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
120 to 340
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
12 to 16
Strength to Weight: Bending, points 27 to 32
14 to 17
Thermal Diffusivity, mm2/s 3.5
14
Thermal Shock Resistance, points 25 to 33
11 to 14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0.15 to 0.35
0.080 to 0.12
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Iron (Fe), % 0 to 0.75
99.17 to 99.6
Manganese (Mn), % 0 to 1.0
0.3 to 0.5
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0
0 to 0.025

Comparable Variants