R31538 Cobalt vs. EN 1.0345 Steel

R31538 cobalt belongs to the cobalt alloys classification, while EN 1.0345 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is EN 1.0345 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 23
27
Fatigue Strength, MPa 310 to 480
170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
420
Tensile Strength: Yield (Proof), MPa 580 to 930
230

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
49
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.3

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 8.1
1.5
Embodied Energy, MJ/kg 110
19
Embodied Water, L/kg 530
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
96
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
140
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
15
Strength to Weight: Bending, points 27 to 32
16
Thermal Diffusivity, mm2/s 3.5
13
Thermal Shock Resistance, points 25 to 33
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0.15 to 0.35
0 to 0.16
Chromium (Cr), % 26 to 30
0 to 0.3
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 0.75
97.2 to 99.38
Manganese (Mn), % 0 to 1.0
0.6 to 1.2
Molybdenum (Mo), % 5.0 to 7.0
0 to 0.080
Nickel (Ni), % 0 to 1.0
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0 to 0.25
0 to 0.012
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020