MakeItFrom.com
Menu (ESC)

R31538 Cobalt vs. EN 1.3538 Steel

R31538 cobalt belongs to the cobalt alloys classification, while EN 1.3538 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is EN 1.3538 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
670 to 740

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1450
Melting Onset (Solidus), °C 1290
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.5

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.1
1.6
Embodied Energy, MJ/kg 110
21
Embodied Water, L/kg 530
56

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
24 to 26
Strength to Weight: Bending, points 27 to 32
22 to 23
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 25 to 33
20 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.15 to 0.35
0.93 to 1.1
Chromium (Cr), % 26 to 30
1.7 to 2.0
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 0.75
96 to 97.2
Manganese (Mn), % 0 to 1.0
0.6 to 0.8
Molybdenum (Mo), % 5.0 to 7.0
0.4 to 0.5
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.030