R31538 Cobalt vs. EN 1.4742 Stainless Steel

R31538 cobalt belongs to the cobalt alloys classification, while EN 1.4742 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is EN 1.4742 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 13 to 23
17
Fatigue Strength, MPa 310 to 480
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 86
77
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
600
Tensile Strength: Yield (Proof), MPa 580 to 930
300

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Melting Completion (Liquidus), °C 1360
1420
Melting Onset (Solidus), °C 1290
1380
Specific Heat Capacity, J/kg-K 450
490
Thermal Conductivity, W/m-K 13
19
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
2.2

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.6
Embodied Carbon, kg CO2/kg material 8.1
2.2
Embodied Energy, MJ/kg 110
32
Embodied Water, L/kg 530
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
84
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
230
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 34 to 45
22
Strength to Weight: Bending, points 27 to 32
21
Thermal Diffusivity, mm2/s 3.5
5.1
Thermal Shock Resistance, points 25 to 33
21

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.2
Carbon (C), % 0.15 to 0.35
0 to 0.12
Chromium (Cr), % 26 to 30
17 to 19
Cobalt (Co), % 58.7 to 68.9
0
Iron (Fe), % 0 to 0.75
77.2 to 81.6
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.0
0.7 to 1.4
Sulfur (S), % 0
0 to 0.015